Dental Sintering Furnace

Dental Sintering Furnace

a larger sintering capacity of up to 80 individual crowns. The heating system with four high-performance molybdenum disilicide heating elements (MoSi2) means that you can now choose whether to use the conventional long-term sintering or the SPEED-sintering with a new improved heating rate up to 120°C/minute. The simple, practical handling of the HT-series program control was also incorporated here with all its familiar functions; program display on a four-line LCD-display, timer function for sintering overnight or also using drying programs for wet-milled restorations. There are three service programs for servicing the heating chamber and the heating system. 60 SINGLE CROWNS or SINTERING DISC 30 programs capacity 9 heating stages High-quality molybdenum-disilicide heating elements PRO Heating-chamber capacity 2x Ø 120/30 mm Program control (LCD-Display, 4 stages, 30 program capacity, Special functions) Service programs A - Temperature control* only in conjunction with test-kit C-Purge heating chamber E- Regenerate heating elements Thermocouple PtRh-Pt, type S Temperature accuracy at 1500°C +/- 3°C Timer function Max. programmable heating rate 120°C/min.

更大的烧结能力，可达80个单个牙冠。带有四个高性能二硅化钼加热元件（MoSi2）的加热系统意味着您现在可以选择是使用传统的长期烧结还是使用SPEED烧结，其加热速率提高到120°C/分钟。HT系列程序控制的简单实用的操作也与它所有熟悉的功能结合在一起；四行LCD显示器上的程序显示、过夜烧结的定时器功能或湿磨修复体的干燥程序。有三个维修程序用于维修加热室和加热系统。60个单冠或烧结盘30个程序容量9个加热阶段高品质二硅化钼加热元件PRO加热室容量2xØ120/30 mm程序控制（LCD显示器，4个阶段，30个程序能力，特殊功能）服务程序A - 温度控制*仅与测试套件C-Purge加热室E-再生加热元件热电偶PtRh-Pt，S型温度精度为1500°C+/-3°C定时器功能最大可编程加热速率120°C/min。

烧结盘的纯度为99.8%，（K2O、Na2O、Fe2O3 ）含量不大于0.10。

烧结盘使用指南：

1、可以长期使用在1550度以下。短时间内可以使用在1600度（保证使用时间2小时内）。

2、在炉温低于380度时打开炉门。此制品一定避免极冷极热，容易导致热胀冷缩不均匀造成开裂。

3、此为陶瓷制品，使用过程中避免有外力磕碰伤。